High Strength Low Alloy Steel
|
High Strength Low Alloy Steel
|
This information provides repair recommendations and general guidelines for steel classified as High Strength Low Alloy Steel, also known as HSLA. This type of steel normally has a tensile strength range from 300-700 MPa.
General Motors recommends the following when repairing or replacing this type of steel during collision repair.
Recommended Repairs
•
|
Cold repairs can be performed on this type of steel, unless the damage includes kinks. If the damage includes kinks, the part should be replaced.
|
•
|
Controlled use of heat can be used to repair damage, if the heat does not exceed 650°C (1200°F). The heat should be applied a maximum of 2 times, for up to 90 seconds.
|
•
|
Sectioning or partial replacement of this type of steel is recommended only at approved locations, in a specific sectioning procedure.
|
•
|
This type of steel can be used as a sleeve, or backer plate, during sectioning procedures.
|
•
|
Squeeze Resistance Spot Welding can be used to replace factory spot welds, where applicable.
|
•
|
MIG plug welding and MIG stitch welding can be used on this type of steel.
|
•
|
MIG Brazing can be used on this type of steel.
|