Structural Adhesive Body Repairs
|
Structural Adhesive Body Repairs
|
Note
|
Specifications for welded, brazed and riveted connections.
|
Note
|
In order to ensure optimal bonding, the assembly components must fit well, the joint flanges must be clean, the prescribed application technique must be followed and working conditions must be good and at the right temperature.
|
Adhesive is a non-metallic material that joins two assembly components through surface bonding (adhesion) and inner cohesiveness (cohesion). An important element of this process is following the prescribed application technique whether in production or for body repair.
|
Upon application of the fluid adhesive, the adhesion and cohesion forces are still low. Curing is complete once the adhesive has become solid. The joint withstands loads in accordance with its design.
|
Good adhesive application (smooth application of adhesive on the surface) on the joint flanges ensures good bonding and adhesion.
|
Poor adhesive application on the joint flanges leads to poor bonding and adhesion.
|
Adhesive Joint Principles
|
Callout
|
Description
|
1
|
Depiction of adhesive forces
|
A chain is formed from:
|
A
|
Adhesion of the adhesive to the top plate
|
B
|
Cohesion within the adhesive layer
|
C
|
Adhesion of the adhesive to the bottom plate
|
2
|
Depiction of good bonding
|
Good coating of assembly components with adhesive
|
3
|
Depiction of poor bonding
|
Poor adhesive coating on assembly component surfaces (for example, due to poor preparation or contamination)
|
Adhesive in the Area of Connection Flanges to the Body
|
Note
|
Knowledge of the stress placed on the joint locations is paramount to achieving optimal adhesive joints.
|
The following applies as a rule of thumb:
1.
|
Permissible types of stresses on adhesive joints: tensile force, shearing force and compression force.
|
2.
|
Peel forces work negatively on the adhesive joint. Use constructive measures to prevent peeling.
|
Effects of Peeling Forces
|
1.
|
Depiction of typical unwanted, linear separation of the adhesive layer (peeling).
|
|
•
|
Fixing with resistance spot-welds or rivets with a spacing of 150 mm (6 in).
|
|
•
|
Use of waterproof steel rivets, if there is access to the body flange.
|
Rivet Length
|
Rivet Diameter
|
Clamping Area (sum total of sheet thicknesses to be joined together)
|
Part No.
|
Catalogue No.
|
8 mm (0.3 in)
|
4 mm (0.2 in)
|
1.5-3.0 mm (0.06-0.1 in)
|
93184033
|
1 84 983
|
9.5 mm (0.4 in)
|
4 mm (0.2 in)
|
3.0-5.0 mm (0.1-0.2 in)
|
93184034
|
1 84 984
|
12 mm (0.5 in)
|
4 mm (0.2 in)
|
6.5-8.5 mm (0.25-0.33 in)
|
93174636
|
1 88 890
|
Stresses to Which Components/Adhesive Joints are Subjected
|
Callout
|
Description
|
1
|
Peeling stress
|
2
|
Tensile stress
|
3
|
Compression stress
|
4
|
Tensile shearing stress
|
5
|
Compression shearing stress
|
Depiction of Flange Joints
|
Callout
|
Description
|
1
|
Offset flange
|
2
|
T-shaped joint
|
3
|
Bracing (U and L flanges)
|
4
|
Scarf joint (cover plate ground to 30-70° (86-158°F) angle
|
5
|
Double lashings
|
6
|
Combination with different profiles
|
7
|
Offset angle profile
|
8
|
Bracing with 3-layer plate
|
Preparation of Bonding Flanges to be Connected
|
1.
|
Note
|
Dirt (X) leads to problems.
|
Grind flange
|
|
•
|
Remove primer at spot welds using graining P100.
|
|
•
|
When assembling with steel rivets, slightly strip primer from the remaining flanges using graining P360.
|
2.
|
Cleaning
Clean/de-grease bonding surfaces before and after grinding (use cleaner from adhesive kit).
|
Use of Structural Adhesive Systems in Production - Consequences in Service
|
Choice of adhesives for use in body shells is based on structural calculations and tests. The approved adhesives must be harmonized with the entire manufacturing process.
The following guidelines apply:
•
|
Short application times
|
•
|
Use of single-component adhesive systems
|
•
|
High hardening temperatures (approx. 180°C) circulating in the drying kilns
|
The service department cannot use the adhesives/adhesive systems from production. Completely new systems must be developed, tested and approved for service.
Thus, adhesive systems and application techniques will be used that are tailored to repair work. The bonding technique developed for service shall be the logical result of a modern, economical, safe joining system for body repair at the dealership.
This is beneficial to our ability to compete in the bodywork repair market. The goal is to further develop and refine work methods in order to generate cost effective solutions and maintain a competitive edge - without sacrificing quality.
Overview of Areas in Which the Adhesive Technique is Already Used for Bodywork Repair
|
Adhesive Kit for Bodywork Repair in Service
|
We carry the adhesive kit for this purpose in the product range as anti-corrosion adhesive sealing system.
Description
|
Color
|
Container
|
Part No.
|
Catalogue No.
|
Storage Stability
(Best-Before Date is Specified on the Cartridge)
|
Anti-corrosion adhesive sealing system (kit)
|
Blue
|
310 ml (10.5 oz)
|
93 160 535
|
15 05 000
|
12 months
|
The anti-corrosion adhesive sealing kit contains a dual component epoxide adhesive.
After hardening, the adhesive has good resistance to tensile shearing, impacts and peeling. The adhesive can be welded with a resistance spot welding machine when wet (observe setting time).
It has excellent bonding properties with properly prepared, clean surfaces (body sheet metal, pre-treated aluminium).
Adhesive Basis (Component A and Component B)
|
Components
|
Description
|
Component A
|
Epoxy resin, color - blue
|
Component B
|
Hardener (polymer amine), color - white
|
Mixture Ratio
|
A:B = 2:1
|
General Handling Instructions
|
•
|
Observe safety data sheet/handling instructions for adhesive kit 93 160 535 / 15 05 000 (www.ifz-berlin.de).
|
•
|
Watch information on handling adhesive systems in videos VT-41 and VT 54.
|
•
|
Adhesive systems are to be bonded to:
|
|
-
|
Body sheet metal, ground to bare metal
|
|
-
|
Primer of our metal service parts, ground primer
|
•
|
Depending on the installation tolerances of the assembly components, adhesive beads between 0.2 mm and 3 mm (0.007-0.11 in) can be adjusted.
|
•
|
Soldering and welding must be done at a safe distance of at least 50 mm (2 in) outside of the adhesive zone (to prevent the adhesive from catching fire or damage to the joint due to burnt adhesive).
|
•
|
When installing new body parts, such as tail lamp corner inserts, apply the bead of adhesive (diameter - min. 4 mm) (0.2 in) to both the body flange and the new part.
|
•
|
For large components, such as the roof, apply the bead of adhesive (diameter - min. 6 mm) (0.2 in) to the new part.
|
•
|
Do not work with adhesive at temperatures is below 15°C (59°F).
|
•
|
Apply and work with the adhesive as quickly as possible.
|
•
|
The adhesive is compatible with sealing and painting material.
|
•
|
After application, the adhesive system can be handled for up to 2 hours at 23°C (73.4°F) in order to join, handle, resistance spot weld or secure fixing rivets to sheet metal parts.
Note
|
The higher the ambient temperature, the shorter the handling time.
|
|
•
|
The adhesive cartridge is intended for use in:
|
|
-
|
Cordless guns (with infinitely adjustable control)
|
|
-
|
Note
|
Use of pneumatic guns without plunger could lead to the incorrect mixture of adhesive during application.
|
Before application, the adhesive components are mixed together in a static mixer in the emulsion tube. The second generation of static mixers, which can be screwed onto the cartridge, have considerable reduced the time needed for adhesive application (see data on time).
|
Increased durability and corrosion protection.
|
Better shielding and sealing of the bonded body flange.
|
Pneumatic guns (with mechanical plunger)
|
•
|
Forced mixture of adhesive components in an emulsion tube before application (static mixer).
|
•
|
Increased durability and corrosion protection of joints.
|
•
|
Shielding and sealing of the bonded body flange.
|
•
|
Reduction of noise emission and vibrations.
|
•
|
Prevention of electrochemical corrosion.
|
•
|
Compatible with sealants and paints.
|
•
|
Reduction of the number of spot welds on the joint flanges through use of adhesive as opposed to conventional resistance spot welding without adhesive.
|
|
-
|
On average, the spacing is 150 mm.
|
|
-
|
This spacing also applies when fixing with our special steel rivets.
|
Time studies were performed to determine the application rate with the adhesive and static mixer. The data in the table is based on application at 21°C with a pneumatic gun - with mechanical plunger only.
Application Time
|
Adhesive Bead Diameter
|
5 mm (0.2 in)
|
8 mm (0.3 in)
|
10 mm (0.4 in)
|
Application time for 1 meter (3 ft)
|
1/2 minute
|
1 minute
|
1 1/2 minutes
|
Application time for 3 meters (10 ft)
|
1 minute
|
2 1/2 minutes
|
4 minutes
|
Application time for 5 meters (16 ft)
|
2 minutes
|
4 1/2 minutes
|
6 1/2 minutes
|
Application time for 7 meters (23 ft)
|
2 1/2 minutes
|
6 minutes
|
8 1/2 minutes
|
Aids in Preventing Use of Incorrect Adhesive Mixture
|
•
|
Ensure there are equal levels of the two adhesive components (see handling instructions).
|
•
|
Note the color of the adhesive mixture:
|
|
-
|
Light blue (homogeneous) correct mixture - continue procedure without interruption.
|
|
-
|
White or dark blue: Incorrect mixture - remove applied material immediately.
|
|
-
|
Application at room temperature -21°C to 23°C (70-73°F).
|
|
-
|
Below 15°C (59°F) application is difficult; the viscosity of the adhesive is too high.
|
|
-
|
15-30°C (59-86°F) is the optimal range for handling.
|
|
-
|
Never heat the adhesive cartridge (heat gun) or place it in hot water.
|
•
|
Hardening of the mixed adhesive
|
Drying Temperature
|
Handling Time of the Attached Body Piece
|
at 60°C (140°F)
|
30 minutes
|
at 30°C (86°F)
|
~ 1 hour
|
at 23°C (73°F)
|
~ 2 hours
|
at 13°C (55°F)
|
~ 4 to 8 hours
|
at 3°C (37°F)
|
~ 16 to 32 hours
|
Adhesive Kit Content 93 160 535 / 15 05 000
|
Note
|
The cartridge gun is not included in the kit.
|
Quantity
|
Description
|
1x
|
Adhesive cartridge with dual component adhesive
Component A (resin) ~ 122 ml (4 oz)
Component B (hardener) ~ 73 ml (2 oz)
|
3x
|
Static mixer, screwable (white)
|
1x
|
Cleaner ~ 100 ml (3 oz)
|
3x
|
Cleaning cloth (green)
|
3x
|
Drying cloth (blue)
|
1x
|
Handling instructions
|
1x
|
Kit packaging
|
Application Devices
In the course of our studies, we focused on 3 types of guns for troublefree handing of adhesive:
•
|
Cordless guns - infinitely adjustable
|
•
|
Pneumatic guns - with mechanical plunger only
|
Average Adhesive Bead Length/Cartridge Capacity
|
The cartridge contents of anti-corrosion adhesive sealant kit 93160535 / 15 05 000 provide an adhesive bead that is about 3.50 m (11 ft) in length on average, depending on the bead thickness.
The cartridge contents of single-component window adhesive 93165025 / 15 04 815 provide an adhesive bead that is about 3.00 m (10 ft) in length on average, depending on the bead thickness.
Explanation of Designations for Joining Techniques
|
Seam Form Field
Seam Quantity Field
1
|
Resistance spot welding (Qty: 9)
|
2
|
Plug spot welding, gas-shielded arc welding (Qty: 9) slot brazing, gas-shielded brazing (Qty: 9)
|
3
|
Quilting seam spot welding/spot brazing with sheet metal overlap, gas-shielded arc welding and gas-shielded brazing (Qty: 9)
|
4
|
Full seam, gas-shielded arc welding and gas-shielded brazing
|
5
|
Full seam, interrupted, gas-shielded arc welding (Qty: 9)
|
6
|
Structural metal adhesive (adhesive, part no. 93 160 535)
|
7
|
Rivets (steel rivets, part no. 93 174 636, Qty: 9)
|
Seam Length Field
Example for seam length:
1.
|
Seam length is always specified with measurement and unit (mm).
|
2.
|
The minimum seam length (lower limit) for applying a full seam is always to be set to 15 mm (0.6 in).
|
3.
|
The following applies to plug welds:
|
|
•
|
Seam length is not applicable, i.e. the seam length is always matches the shape of the round hole or slot.
|
|
•
|
The hole must be completely filled, i.e. the seam must completely cover the hole.
|
|
•
|
In the event of top bead depression, rewelding is required (thickness of the seam).
|
Joining Method Field
1.
|
Resistance spot welding
|
3.
|
Gas-shielded MIG brazing
|
4.
|
Structural Metal Adhesive
|